Purpose: To examine the bond strength and interfacial nanoleakage expression of fiber posts luted to intraradicular dentin with self-adhesive cements. Six-month and 1-year aging effects were examined. Materials and Methods: Post space was created in endodontically treated human incisors. Each tooth was assigned to a self-adhesive cement/post combination: (1) Bifix SE Cement (Voco) with proprietary posts (Rebilda Post, Voco), (2) RelyX Unicem (3M ESPE) with proprietary posts (Rely X Fiber Post, 3M ESPE), (3) MaxCem (Kerr) with Rebilda Posts. Each specimen was cut into 1-mm-thick sections and either immediately stressed to failure with the push-out bond strength test or aged in artificial saliva for 6 months or 1 year before testing. Additional specimens were processed for quantitative interfacial nanoleakage analysis using ammoniacal silver nitrate. Results: Immediate bond strength ranked in the following order: Bifix SE (7.8 ± 2.9 MPa) = RelyX Unicem (8.4 ± 2.7 MPa) > MaxCem (4.6 ± 2.4 MPa) (p < 0.05). Aging significantly reduced the bond strength of all cements after 1 year: Bifix SE (3.8 ± 1.4 MPa) = RelyX Unicem (5.8 ± 1.7 MPa) > MaxCem (1.3 ± 0.9 MPa; p<0.05). No immediate difference in interfacial nanoleakage expression was found. Nanoleakage increased after aging, and MaxCem showed the highest values. Conclusion: The push-out strength and interfacial nanoleakage expression of fiber posts luted with self-adhesive cements were dependent on luting material and type of post, and were significantly affected by storage time. © 2013 by Quintessence Publishing Co Inc.

Marchesi, G., Mazzoni, A., Turco, G., Cadenaro, M., Ferrari, M., Di Lenarda, R., et al. (2013). Aging affects the adhesive interface of posts luted with self-adhesive cements: a 1-year study. JOURNAL OF ADHESIVE DENTISTRY, 15(2), 173-180 [10.3290/j.jad.a28387].

Aging affects the adhesive interface of posts luted with self-adhesive cements: a 1-year study

Ferrari, Marco;
2013-01-01

Abstract

Purpose: To examine the bond strength and interfacial nanoleakage expression of fiber posts luted to intraradicular dentin with self-adhesive cements. Six-month and 1-year aging effects were examined. Materials and Methods: Post space was created in endodontically treated human incisors. Each tooth was assigned to a self-adhesive cement/post combination: (1) Bifix SE Cement (Voco) with proprietary posts (Rebilda Post, Voco), (2) RelyX Unicem (3M ESPE) with proprietary posts (Rely X Fiber Post, 3M ESPE), (3) MaxCem (Kerr) with Rebilda Posts. Each specimen was cut into 1-mm-thick sections and either immediately stressed to failure with the push-out bond strength test or aged in artificial saliva for 6 months or 1 year before testing. Additional specimens were processed for quantitative interfacial nanoleakage analysis using ammoniacal silver nitrate. Results: Immediate bond strength ranked in the following order: Bifix SE (7.8 ± 2.9 MPa) = RelyX Unicem (8.4 ± 2.7 MPa) > MaxCem (4.6 ± 2.4 MPa) (p < 0.05). Aging significantly reduced the bond strength of all cements after 1 year: Bifix SE (3.8 ± 1.4 MPa) = RelyX Unicem (5.8 ± 1.7 MPa) > MaxCem (1.3 ± 0.9 MPa; p<0.05). No immediate difference in interfacial nanoleakage expression was found. Nanoleakage increased after aging, and MaxCem showed the highest values. Conclusion: The push-out strength and interfacial nanoleakage expression of fiber posts luted with self-adhesive cements were dependent on luting material and type of post, and were significantly affected by storage time. © 2013 by Quintessence Publishing Co Inc.
2013
Marchesi, G., Mazzoni, A., Turco, G., Cadenaro, M., Ferrari, M., Di Lenarda, R., et al. (2013). Aging affects the adhesive interface of posts luted with self-adhesive cements: a 1-year study. JOURNAL OF ADHESIVE DENTISTRY, 15(2), 173-180 [10.3290/j.jad.a28387].
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11365/983177
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo