PURPOSE: To evaluate the effect of different curing modes of dual-curing luting systems and root regions on the push-out strength of fiber posts to intraradicular dentin. MATERIALS AND METHODS: Forty-two extracted premolars with a single root canal were sectioned at the cementoenamel junction and the roots were endodontically treated. The roots were divided into two groups according to two dual-curing luting systems: (1) XP BOND-Dual Cure/Calibra resin cement; (2) XP BOND-Dual Cure/FluoroCore 2. For each luting system, three different curing modes were applied to the dentin adhesive and resin cement: "Self-cure and Self-cure (SC&SC)", "Self-cure and Dual-cure (SC&DC)", and "Dual-cure and Dual-cure (DC&DC)". Translucent Easy fiber posts (Dentsply Maillefer) were luted in the roots. A thin-slice push-out test was performed, and the data of push-out strength were analyzed using three-way ANOVA with luting system, curing mode, and root region (apical, middle and coronal) as factors. Tukey's test was used for post-hoc comparisons. RESULTS: The push-out strength of XP BOND-Dual Cure/Calibra was significantly lower when Calibra resin cement was self-cured than when it was dual-cured (SC&SC: 6.04 +/- 2.65 MPa; SC&DC: 10.69 +/- 3.01 MPa; DC&DC: 10.72 +/- 3.63 MPa; p < 0.05). The curing modes did not affect the push-out strength of XP BOND-Dual Cure/FluoroCore 2 (SC&SC: 7.90 +/- 3.94 MPa; SC&DC: 8.32 +/- 2.73 MPa; DC&DC: 9.27 +/- 4.12 MPa; p > 0.05). The coronal push-out strength was significantly higher than the apical push-out strength (p < 0.05). CONCLUSION: Retention of fiber posts in root canals was affected by the curing modes of dual-curing luting system and root regions.

Zhang, L., Magni, E., Radovic, I., Wang, Y.j., Chen, J.h., Ferrari, M. (2008). Effect of curing modes of dual-curing luting systems and root regions on retention of translucent fiber posts in root canals. JOURNAL OF ADHESIVE DENTISTRY, 10(3), 219-226.

Effect of curing modes of dual-curing luting systems and root regions on retention of translucent fiber posts in root canals.

FERRARI, MARCO
2008-01-01

Abstract

PURPOSE: To evaluate the effect of different curing modes of dual-curing luting systems and root regions on the push-out strength of fiber posts to intraradicular dentin. MATERIALS AND METHODS: Forty-two extracted premolars with a single root canal were sectioned at the cementoenamel junction and the roots were endodontically treated. The roots were divided into two groups according to two dual-curing luting systems: (1) XP BOND-Dual Cure/Calibra resin cement; (2) XP BOND-Dual Cure/FluoroCore 2. For each luting system, three different curing modes were applied to the dentin adhesive and resin cement: "Self-cure and Self-cure (SC&SC)", "Self-cure and Dual-cure (SC&DC)", and "Dual-cure and Dual-cure (DC&DC)". Translucent Easy fiber posts (Dentsply Maillefer) were luted in the roots. A thin-slice push-out test was performed, and the data of push-out strength were analyzed using three-way ANOVA with luting system, curing mode, and root region (apical, middle and coronal) as factors. Tukey's test was used for post-hoc comparisons. RESULTS: The push-out strength of XP BOND-Dual Cure/Calibra was significantly lower when Calibra resin cement was self-cured than when it was dual-cured (SC&SC: 6.04 +/- 2.65 MPa; SC&DC: 10.69 +/- 3.01 MPa; DC&DC: 10.72 +/- 3.63 MPa; p < 0.05). The curing modes did not affect the push-out strength of XP BOND-Dual Cure/FluoroCore 2 (SC&SC: 7.90 +/- 3.94 MPa; SC&DC: 8.32 +/- 2.73 MPa; DC&DC: 9.27 +/- 4.12 MPa; p > 0.05). The coronal push-out strength was significantly higher than the apical push-out strength (p < 0.05). CONCLUSION: Retention of fiber posts in root canals was affected by the curing modes of dual-curing luting system and root regions.
2008
Zhang, L., Magni, E., Radovic, I., Wang, Y.j., Chen, J.h., Ferrari, M. (2008). Effect of curing modes of dual-curing luting systems and root regions on retention of translucent fiber posts in root canals. JOURNAL OF ADHESIVE DENTISTRY, 10(3), 219-226.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11365/34582
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo