A new phosphorylated derivative of carboxymethylcellulose and amidic carboxymethylcellulose containing one phosphate group for each disaccharide unit was synthesized using sodium trimetaphospahte (STMP) as the phosphating agent. The new polysaccharide was characterized by infrared spectroscopy (FT-IR) and the amount of phosphate groups was determined by elemental analysis. These modified polysaccharides were used both to prepare 3D scaffolds and functionalize titanium oxide surfaces with the aim to improve the osseointegration with the host tissue. The presence of phosphate groups modify the physical-chemical properties of the hydrogels with respect to the native ones. The evaluation of the bioactivity of the phosphorylated carboxymethylcellulose hydrogels towards osteoblast-like cells showed a significant increase in the osteocalcin production. The modified surfaces were chemically characterized by means of X-ray photoelectron spectroscopy (XPS) and FT-IR, whereas the surface topography was analysed by Atomic Force Measurements (AFM) measurements before and after the polysaccharide coating. In vitro biological tests using osteoblast-like cells demonstrated that phosphorylated carboxymethylcellulose functionalized TiO2 surfaces promoted better cell adhesion and significantly enhanced their proliferation. These findings suggest that the phosphate polysaccharide both as a 3D scaffold and as a surface coating promotes osteoblast growth potentially improving the biomaterial osseointegration rate.

Pasqui, D., Danieli, E., Leone, G., Torricelli, P., Barbucci, R. (2008). A new Phosphorylated Polysaccharide for Biomedical Applications: Generation of 3D Scaffolds with Osteogenic Activity and Coating of Titanium Oxide Surfaces. MACROMOLECULAR SYMPOSIA, 266(1), 23-29 [10.1002/masy.200850605].

A new Phosphorylated Polysaccharide for Biomedical Applications: Generation of 3D Scaffolds with Osteogenic Activity and Coating of Titanium Oxide Surfaces

Leone, Gemma;Barbucci, Rolando
2008-01-01

Abstract

A new phosphorylated derivative of carboxymethylcellulose and amidic carboxymethylcellulose containing one phosphate group for each disaccharide unit was synthesized using sodium trimetaphospahte (STMP) as the phosphating agent. The new polysaccharide was characterized by infrared spectroscopy (FT-IR) and the amount of phosphate groups was determined by elemental analysis. These modified polysaccharides were used both to prepare 3D scaffolds and functionalize titanium oxide surfaces with the aim to improve the osseointegration with the host tissue. The presence of phosphate groups modify the physical-chemical properties of the hydrogels with respect to the native ones. The evaluation of the bioactivity of the phosphorylated carboxymethylcellulose hydrogels towards osteoblast-like cells showed a significant increase in the osteocalcin production. The modified surfaces were chemically characterized by means of X-ray photoelectron spectroscopy (XPS) and FT-IR, whereas the surface topography was analysed by Atomic Force Measurements (AFM) measurements before and after the polysaccharide coating. In vitro biological tests using osteoblast-like cells demonstrated that phosphorylated carboxymethylcellulose functionalized TiO2 surfaces promoted better cell adhesion and significantly enhanced their proliferation. These findings suggest that the phosphate polysaccharide both as a 3D scaffold and as a surface coating promotes osteoblast growth potentially improving the biomaterial osseointegration rate.
2008
Pasqui, D., Danieli, E., Leone, G., Torricelli, P., Barbucci, R. (2008). A new Phosphorylated Polysaccharide for Biomedical Applications: Generation of 3D Scaffolds with Osteogenic Activity and Coating of Titanium Oxide Surfaces. MACROMOLECULAR SYMPOSIA, 266(1), 23-29 [10.1002/masy.200850605].
File in questo prodotto:
File Dimensione Formato  
full_text.pdf

non disponibili

Tipologia: Post-print
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 164.58 kB
Formato Adobe PDF
164.58 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11365/34264
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo