The influence of thermocycling on the bond strength of fibre posts cemented with different luting approaches was investigated. A total of 84 human incisors were selected for the study. Sixty teeth were assigned to one of the following adhesive/cement combinations for push-out bond-strength evaluation: group 1, XP Bond/CoreXFlow + DT Light-Post; group 2, Panavia F 2.0 + Tech 21; or group 3, RelyX Unicem + RelyX. Bonded specimens were cut into 1-mm-thick slabs and either thermocycled (40,000 cycles) or stored in artificial saliva (control specimens) before push-out bond-strength testing. Additional specimens were processed for quantitative interfacial nanoleakage analysis. Thermocycling decreased the bond strength in specimens of groups 2 and 3, but did not affect the specimens from group 1. No difference was observed among luting approaches in control specimens. Thermocycling resulted in increased silver nitrate deposition (i.e. interfacial nanoleakage) in all groups. Within the limitations of the study, the use of an etch-and-rinse adhesive in combination with a dual-cure cement to lute fiber posts is the most stable luting procedure if compared with a self-etch resin-based cement or a self-adhesive cement, as assayed by thermocycling of the bonded specimens.

Mazzoni, A., Marchesi, G., Cadenaro, M., Mazzotti, G., DI LENARDA, R., Ferrari, M., et al. (2009). Push-out stress for fibre posts luted using different adhesive strategies. EUROPEAN JOURNAL OF ORAL SCIENCES, 117(4), 447-453.

Push-out stress for fibre posts luted using different adhesive strategies

FERRARI, MARCO;
2009-01-01

Abstract

The influence of thermocycling on the bond strength of fibre posts cemented with different luting approaches was investigated. A total of 84 human incisors were selected for the study. Sixty teeth were assigned to one of the following adhesive/cement combinations for push-out bond-strength evaluation: group 1, XP Bond/CoreXFlow + DT Light-Post; group 2, Panavia F 2.0 + Tech 21; or group 3, RelyX Unicem + RelyX. Bonded specimens were cut into 1-mm-thick slabs and either thermocycled (40,000 cycles) or stored in artificial saliva (control specimens) before push-out bond-strength testing. Additional specimens were processed for quantitative interfacial nanoleakage analysis. Thermocycling decreased the bond strength in specimens of groups 2 and 3, but did not affect the specimens from group 1. No difference was observed among luting approaches in control specimens. Thermocycling resulted in increased silver nitrate deposition (i.e. interfacial nanoleakage) in all groups. Within the limitations of the study, the use of an etch-and-rinse adhesive in combination with a dual-cure cement to lute fiber posts is the most stable luting procedure if compared with a self-etch resin-based cement or a self-adhesive cement, as assayed by thermocycling of the bonded specimens.
2009
Mazzoni, A., Marchesi, G., Cadenaro, M., Mazzotti, G., DI LENARDA, R., Ferrari, M., et al. (2009). Push-out stress for fibre posts luted using different adhesive strategies. EUROPEAN JOURNAL OF ORAL SCIENCES, 117(4), 447-453.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11365/33986
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo