Effect of sandblasting and/or priming treatment on the shear bond strength of self-adhesive resin cement to CAD/CAM blocks

The aim of this study was to investigate the effect of two different priming agents and/or sandblasting on the shear bond strength of self-adhesive resin cement to the resin composite for core build-up to CAD/CAM blocks. A CAD/CAM ceramic block (GN I CERAMIC BLOCK, GC) and a CAD/CAM resin composite block (CERASMART 270, GC), a self-adhesive resin cement (G-CEM ONE, GC) and two different primers, i.e., a multipurpose primer (MP; G-Multi Primer, GC) and a ceramic primer (CP; Ceramic Primer II, GC), were examined. Five different surface treatments with priming and/or sandblasting and no surface treatment (control) were performed on the block. Disk specimens (6 mm in diameter and 4 mm in thickness) made from core composites were cemented to the blocks after the surface treatments. Then, the 24-h shear bond strength of the resin cement between the block and the resin composite core was determined (n = 15). Sandblasted specimens had greater bond strength than controls for both blocks (p < 0.05). Priming to both blocks significantly increased the bond strength of resin cement compared to that of controls (p < 0.05). Although Weibull moduli were not significantly changed among all surface treatments for both blocks, the strengths with 5% and 95% failure probability of sandblasted and/or primed blocks were estimated to be greater than those of controls. The combination of priming and sandblasting to the CAD/CAM composite and ceramic surface was effective in increasing the bond strength of the resin cement.