PURPOSE: This study investigated the microtensile bond strength of three different ceramic veneering systems to one type of zirconia substrate. METHODS: Bilayered zirconia veneer discs were fabricated of a LAVA zirconia core and three different veneering ceramics (VITA VM9, Lava Ceram, Creation ZI) using a conventional layering technique. Discs were cut into microbars of 6 mm x 1 mm x 1 mm. Microtensile bond strength between veneer and core was measured. Surfaces of fractured specimens were examined with scanning electron microscopy (SEM). RESULTS: The mean microtensile bond strengths were respectively VITA VM9 23.52 MPa (8.33), Creation ZI 18.35 MPa (6.40), and Lava Ceram 14.76 MPa (4.00). The differences were statistically significant. Failures were mainly interfacial in all tested groups

Fazi, G., Vichi, A., Ferrari, M. (2010). Microtensile bond strength of three different veneering porcelain systems to a zirconia core for all ceramic restorations. AMERICAN JOURNAL OF DENTISTRY, 23(6), 347-350.

Microtensile bond strength of three different veneering porcelain systems to a zirconia core for all ceramic restorations

VICHI A.;FERRARI M.
2010-01-01

Abstract

PURPOSE: This study investigated the microtensile bond strength of three different ceramic veneering systems to one type of zirconia substrate. METHODS: Bilayered zirconia veneer discs were fabricated of a LAVA zirconia core and three different veneering ceramics (VITA VM9, Lava Ceram, Creation ZI) using a conventional layering technique. Discs were cut into microbars of 6 mm x 1 mm x 1 mm. Microtensile bond strength between veneer and core was measured. Surfaces of fractured specimens were examined with scanning electron microscopy (SEM). RESULTS: The mean microtensile bond strengths were respectively VITA VM9 23.52 MPa (8.33), Creation ZI 18.35 MPa (6.40), and Lava Ceram 14.76 MPa (4.00). The differences were statistically significant. Failures were mainly interfacial in all tested groups
2010
Fazi, G., Vichi, A., Ferrari, M. (2010). Microtensile bond strength of three different veneering porcelain systems to a zirconia core for all ceramic restorations. AMERICAN JOURNAL OF DENTISTRY, 23(6), 347-350.
File in questo prodotto:
File Dimensione Formato  
2010d Am J Dent. Microtensile bond strength of three different porcelain veneering systems to a Zirconia core for all ceramic restorations.pdf

non disponibili

Tipologia: Post-print
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 371.61 kB
Formato Adobe PDF
371.61 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11365/10279
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo